HIPS

It is a printing material that is completely soluble in limonene, there will be no residue on the surface of the model after dissolution, and the contact surface is smooth and flat; its printing performance is similar to ABS, and can be used for ABS, PETG and other materials to print extremely complex shapes or a supporting material having the shape of a partially enclosed chamber; suitable for multi-nozzle printers.

Color:
Diameter Size:
Net Weight:
Personal Purchase:

Introduction

Parameter Information

Notes

Download

* Description:

Description

It is a printing material that is completely soluble in limonene, there will be no residue on the surface of the model after dissolution, and the contact surface is smooth and flat; its printing performance is similar to ABS, and can be used for ABS, PETG and other materials to print extremely complex shapes or a supporting material having the shape of a partially enclosed chamber; suitable for multi-nozzle printers.

Sellingpoint

Solubility
Support
Heat resistance

High toughness
High impact resistance

* Application
Support material Machinery
Filament Properties Table
3D PRINTING FILAMENT HIPS
Density(g/cm3) 1.05
Heat Distortion Temp(℃,0.45MPa) 80
Melt Flow Index(g/10min) 3(200℃/5kg)
Tensile Strength(MPa) 27
Elongation at Break(%) 55
Flexural Strength(MPa) 39
Flexural Modulus(MPa) 2280
IZOD Impact Strength(kJ/㎡) 11
Durability 7/10
Printability 6/10
 

Recommended printing parameters

Extruder Temperature(℃) 230 – 270℃
Recommended temperature:250℃
Bed temperature(℃)  100 – 115°C
Fan Speed  0%
Printing Speed  40 – 100mm/s
Heated Bed  Required
Recommended Build Surfaces Glass plate, PVP solid glue, high temperature tape
Feature
Flexible ——
Elastic ——
Impact Resistant
Soft ——
Composite ——
 UV Resistant ——
Water Resistant ——
Dissolvable
Heat Resistant
Chemically Resistant ——
Fatigue Resistant ——
Need drying ——
Heated Bed Required
Print recommend Minimize the overhang angle structure in the model

1.HIPS has a large shrinkage rate, so you should pay attention to heat preservation when printing, and print in a printer with a closed chamber.
2. It is recommended to set the distance between the support and the model to 0, the first contact layer to slow down and turn off the blowing fan to improve the bonding strength with the main material.