Hard-Tough Resin

Tough; Higher toughness and impact resistance than normal ABS like resin
Can print rugged and durable parts
Excellent mechanical properties. Printed object can be drilled , which is very suitable for mechanical prototypes.

Color:
Net Weight:
Personal Purchase:

Introduction

Parameter Information

Notes

Download

* Description:

Description

Tough;,Higher toughness and impact resistance than normal ABS like resin.
Can print rugged and durable parts.
Excellent mechanical properties. Printed object can be drilled , which is very suitable for mechanical prototypes.

Sellingpoint

High toughness
High impact resistance

Strong and durable

* Product introduction video
* Application
Automobile Mechanical
* Print model
  • Hard-Tough Resin_Print model
  • Hard-Tough Resin_White Print model
  • Hard-Tough Resin_Blue Print model
  • Hard-Tough Resin_Gary Print model
 3D PRINTING PHOTOPOLYMER RESIN Properties Table
3D PRINTING PHOTOPOLYMER RESIN Hard-Tough Resin
Viscosity(mPa·s) 200-300
Density(g/cm3) 1.08-1.12
Tensile Strength(MPa) 30-60
Elongation at Break(%) 35-52
Flexural Strength(MPa) 30-75
Impact Strength(J/m) 40-110
Tearing Strength(GPa) /
Heat Distortion Temp(℃) /
Hardness(Shore D)  75-81
Grades (out of 10)
Strength(S)  8
Toughness(F)  9
Forming(P)  8
Accuracy(S)  7
Speed (A)  8

 

Recommended printing parameters
Settings Machine Type
Low Light Intensity Medium Light Intensity High Light Intensity (Monochrome LCD Screen)
Representative Machine AnyCubic Photon eSUN LCD 3.0
Nova Bene 4
Creality LD-002R
Anycubic MONO X
ELEGOO Saturn
Phrozen Sonic Mini
Exposure Time/s 8-10 5-6 Not recommended
Bottom Layer Count 3-5
Bottom Exposure Time 40-60 30-40 Not recommended
Lifting Distance/mm 5.5&6-inch screen:5-6 or Higher ; 8.9&13.3-inch screen:8-12 or Higher
Lift Speed/mm·min-1  90-150  90-120  Not recommended
Retract Speed/mm·min-1    150-200

1.Shake well before printing
2.Hard tough resin need to be fully cured to achieve the best mechanical strength, it is recommended to cure for 25-30 minutes, the surface cure until it is not sticky hand