Castable resin for Dental

The resin is developed for dental casting; very little burning ash and residues, good casting performance; high precision, printing details are clearly visible; low shrinkage performance, the printed model is not easy to deform.

Color:
Net Weight:

Introduction

Parameter Information

Notes

Download

* Description:

Description

The resin is developed for dental casting; very little burning ash and residues, good casting performance; high precision, printing details are clearly visible; low shrinkage performance, the printed model is not easy to deform.

Sellingpoint

Ash Free

High precision

* Application
Dentistry
* Print model
  • castable resin for dental_1
  • castable resin for dental_4
  • castable resin for dental_3
  • castable resin for dental_2
 3D PRINTING PHOTOPOLYMER RESIN Properties Table
3D PRINTING PHOTOPOLYMER RESIN Castable resin for Dental
Viscosity(mPa·s) 100-150
Density(g/cm3) 1.05-1.12
Tensile Strength(MPa) 42-62
Elongation at Break(%) 11-20
Flexural Strength(MPa) 49-58
Impact Strength(J/m) 44-49
Tearing Strength(GPa) /
Heat Distortion Temp(℃) /
Hardness(Shore D)  80
Grades (out of 10)
Strength(S)  8
Toughness(F)  7
Forming(P)  9
Accuracy(S)  8
Speed (A)  4

 

Recommended printing parameters
Settings Machine Type
Low Light Intensity Medium Light Intensity High Light Intensity (Monochrome LCD Screen)
Representative Machine AnyCubic Photon eSUN LCD 3.0
Nova Bene 4
Creality LD-002R
Anycubic MONO X
ELEGOO Saturn
Phrozen Sonic Mini
Exposure Time/s 26-34 15-20 Not recommended
Bottom Layer Count 3-5
Bottom Exposure Time 130-200 80-120 Not recommended
Lifting Distance/mm 5.5&6-inch screen:5-6 or Higher ; 8.9&13.3-inch screen:8-12 or Higher
Lift Speed/mm·min-1  90-150  90-120  Not recommended
Retract Speed/mm·min-1    150-200

1. Shake well before printing.
2. The dental mold resin can increase the bottom exposure time to enhance the adhesion of the bottom plate.