ABS+HS
ABS+HS is a modified version of ABS material. Compared to conventional ABS, it exhibits lower shrinkage and superior interlayer adhesion, reducing the likelihood of warping and cracking during printing. It contains low VOC (Volatile Organic Compounds) components, resulting in a reduced odor during the printing process, making it more comfortable and stress-free. This material is optimized for high-speed printing, maintaining its performance even at higher speeds, providing an excellent printing experience. Additionally, it can be acetone polished to eliminate layer lines and further enhance the print quality.
- * Description:
-
Description
ABS+HS is a modified version of ABS material. Compared to conventional ABS, it exhibits lower shrinkage and superior interlayer adhesion, reducing the likelihood of warping and cracking during printing. It contains low VOC (Volatile Organic Compounds) components, resulting in a reduced odor during the printing process, making it more comfortable and stress-free. This material is optimized for high-speed printing, maintaining its performance even at higher speeds, providing an excellent printing experience. Additionally, it can be acetone polished to eliminate layer lines and further enhance the print quality.
Features
Heat resistance
Low odor
Low shrinkage rate
Strong performance and toughnessHigh speed printing
Acetone polishing is available
Excellent printabilityReview
- * Product introduction video
-
- * Application
- * Print model
-
1. The shrinkage rate of ABS+ material is large, so you should pay attention to heat preservation when printing, and print in a printer with a closed chamber. 2. The cooling of ABS+ is slightly worse. You can turn on a fan to improve the printing effect, or reduce the drape angle structure in the model; or try to reduce the speed to print.
-
eABS+HS HS Parameters for
Bambu Lab & Creality -
MSDS -
ROHS -
eABS+HS Filament-TDS
| Density(g/cm3) | 1.04 |
| Melt Flow Index | 6(220℃/10kg） |
| Heat Distortion Temp(℃,0.45MPa) | 89 |
| Tensile Strength(MPa) (XY) | 41.64 |
| Tensile Strength(MPa)(Z) | 27.08 |
| Elongation at Break(%)(XY) | 5.14 |
| Elongation at Break(%)(Z) | 3.4 |
| Flexural Strength(MPa)(XY) | 46 |
| Flexural Strength(MPa)(Z) | 44.5 |
| Flexural Modulus(MPa)(XY) | 2349.32 |
| Flexural Modulus(MPa)(Z) | 1934.88 |
| IZOD Impact Strength(kJ/㎡)(XY) | 25.94 |
| IZOD Impact Strength(kJ/㎡)(Z) | 3.14 |
| Extruder Temperature(℃) | 230-270℃ |
| Bed temperature(℃) | 95-110℃ |
| Fan Speed(％) | 0% |
| Printing Speed(mm/S) | 50-300mm/s |
| Heated Bed | Need |
| Printing Suggestions | Sealed box printing |