eResin-PMMA Like
High transparency and anti-yellowing. The visual effect is similar to transparent thermoplatic such as PMMA. Excellent transparency after post-processing( polishing, spraying UV high-transmitting oil). Excellent internal transparency is more suitable for shape and assembly verification. Can print transparent models with high definition and fine details.
- * Description:
-
Description
High transparency and anti-yellowing. The visual effect is similar to transparent thermoplatic such as PMMA. Excellent transparency after post-processing( polishing, spraying UV high-transmitting oil). Excellent internal transparency is more suitable for shape and assembly verification. Can print transparent models with high definition and fine details.
Sellingpoint
High transparency
Yellowing resistance
- * Application
- * Print model
-
| 3D PRINTING PHOTOPOLYMER RESIN Properties Table | |
|---|---|
| 3D PRINTING PHOTOPOLYMER RESIN | eResin-PMMA Like |
| Viscosity(mPa·s) | 300 |
| Density(g/cm3) | 1.05-1.15 |
| Tensile Strength(MPa) | 58 |
| Elongation at Break(%) | 10 |
| Flexural Strength(MPa) | 30 |
| Impact Strength(J/m) | 15 |
| Tearing Strength(GPa) | / |
| Heat Distortion Temp(℃) | / |
| Hardness(Shore D) | 70 |
| Grades (out of 10) | |
| Strength（S） | 6 |
| Toughness（F） | 6 |
| Forming（P） | 8 |
| Accuracy（S） | 8 |
| Speed （A） | 4 |
| Recommended printing parameters | |||
| Settings | Machine Type | ||
| Low Light Intensity | Medium Light Intensity | High Light Intensity (Monochrome LCD Screen) | |
| Representative Machine | AnyCubic Photon | eSUN LCD 3.0 Nova Bene 4 Creality LD-002R |
Anycubic MONO X ELEGOO Saturn Phrozen Sonic Mini |
| Exposure Time/s | 18-24 | 12-16 | 4-6 |
| Bottom Layer Count | 3-5 | ||
| Bottom Exposure Time | ≥80 | ≥60 | ≥30 |
| Lifting Distance/mm | 5.5&6-inch screen：5-6 or Higher; 8.9&13.3-inch screen：8-12 or Higher | ||
| Lift Speed/mm·min-1 | 90-150 | 90-120 | 50-90 |
| Retract Speed/mm·min-1 | 150-200 | ||
1.Shake well before printing
2.Resins need to avoid exposure to light for long time,stored in a place with high air humidity,the printer should be covered when printing, the material in the tank to avoid indoor light exposure. the material in the tank to avoid indoor light exposure,
3.After the model is printed and cleaned with 95% alcohol, it needs to be cured with UV lamp for 1-2min to avoid the influence of air humidity on the model. The printed resin needs to be stored in a bottle alone and should not be put back into the original bottle
4.If the post-curing time is too long, it can be placed for a period of time, and the model will fade yellow. You can also use the microwave to retreat the yellow and red, soak in hot water and put it in the microwave for 30 seconds
5. Post-processing steps: first grinding and polishing, generally from low-eye sandpaper grinding to high-eye sandpaper grinding, such as 400 mesh →600 mesh →800 mesh (the higher the number of grinding mesh, the higher the transparency of spraying oil), grinding and then spraying anti-UV high light oil can achieve the best transparency effect
-
MSDS -
TDS