PLA-Matte Refilament with eSpool+
ePLA-Matte refill is spooless. This matte pla filament 1.75mm can be paired with reusuable spools . Energy saving and environmental protection, save production and transportation costs, reduce carbon emissions.
- * Description:
-
Description
Matte pla filament has no smell when printing, which is safe and environmentally friendly; The matte pla surface is delicate and does not show layer lines; the filament is not easy to break which made the printing is smooth for a long time without clogging. The matte pla filament 1.75mm can be used for early concept models and rapid prototyping.
Sellingpoint
Environmental friendly
Cost-effective
High-speed printing
Easy to peel off the supportExcellent printability
Hard to break
Matte surface effect
Low densityView more about PLA Filament
- * Application
- * Print model
-
| Filament Properties Table | |
|---|---|
| 3D PRINTING FILAMENT | ePLA-Matte Refill |
| Density(g/cm3) | 1.174 |
| Heat Distortion Temp(℃,0.45MPa) | 51 |
| Melt Flow Index(g/10min) | 2.1（190℃/2.16kg） |
| Tensile Strength(MPa) | 34.56 |
| Elongation at Break(%) | 56.1 |
| Flexural Strength(MPa) | 41.21 |
| Flexural Modulus(MPa) | 1119.41 |
| IZOD Impact Strength(kJ/㎡) | 6.2 7/10 |
| Durability | 4/10 |
| Printability | 9/10 |
| Recommended printing parameters | |
| Extruder Temperature(℃) | 190 – 230℃ Recommended temperature 215℃ |
| Bed temperature(℃) | 45 – 60°C |
| Fan Speed | 100% |
| Printing Speed | 40 – 100mm/s |
| Heated Bed | Optional |
| Recommended Build Surfaces | Masking paper, PVP solid glue, PEI |
| Feature | |
| Flexible | —— |
| Elastic | —— |
| Impact Resistant | —— |
| Soft | —— |
| Composite | —— |
| UV Resistant | —— |
| Water Resistant | —— |
| Dissolvable | —— |
| Heat Resistant | —— |
| Chemically Resistant | —— |
| Fatigue Resistant | —— |
| Need drying | —— |
| Heated Bed Required | —— |
| Print recommend | —— |
ePLA-Matte lines are softer than other lines, so the extruder’s tightness adjustment is better not to be too tight, in case to affect printing