eMate（Low temperature PCL）
PCL-based biodegradable material has good toughness and impact resistance; the printing temperature of 70°C makes it safer than high-temperature PLA and ABS; an excellent material companion for 3D printing pens; after printing, the material can be placed in 60°C water to change the shape which can be used as a handmade material and be recycled.
- * Description:
-
Description
PCL-based biodegradable material has good toughness and impact resistance; the printing temperature of 70°C makes it safer than high-temperature PLA and ABS; an excellent material companion for 3D printing pens; after printing, the material can be placed in 60°C water to change the shape which can be used as a handmade material and be recycled.
Sellingpoint
Printed at Low temperature
Safe
Easy to shape by hand
High toughness
High impact resistance
- * Application
- * Print model
-
| Filament Properties Table | |
|---|---|
| 3D PRINTING FILAMENT | eMate |
| Density(g/cm3) | 1.16 |
| Heat Distortion Temp(℃,0.45MPa) | 45 |
| Melt Flow Index(g/10min) | 0.5(70℃/2.16kg) |
| Tensile Strength(MPa) | 18 |
| Elongation at Break(%) | >800 |
| Flexural Strength(MPa) | 13 |
| Flexural Modulus(MPa) | 345 |
| IZOD Impact Strength(kJ/㎡) | Keep on |
| Durability | 4/10 |
| Printability | 6/10 |
| Recommended printing parameters | |
| Extruder Temperature(℃) | 70-100℃ |
| Bed temperature(℃) | 0°C |
| Fan Speed | 100% |
| Printing Speed | 10-20mm/s |
| Heated Bed | —— |
| Recommended Build Surfaces | —— |
| Feature | |
| Flexible | √ |
| Elastic | √ |
| Impact Resistant | √ |
| Soft | √ |
| Composite | —— |
| UV Resistant | —— |
| Water Resistant | —— |
| Dissolvable | —— |
| Heat Resistant | —— |
| Chemically Resistant | —— |
| Fatigue Resistant | —— |
| Need drying | —— |
| Heated Bed Required | √ |
| Print recommend | —— |
Avoid high temperature during storage
-
REACH -
ROHS -
TDS