ABS Odorless

Based on the modification of ABS material, it retains good mechanical properties, lower odor and lower shrinkage rate than conventional ABS materials.With low VOC volatile content, low odor during printing, comfortable printing without pressure; good toughness and impact resistance, it can be used to print sturdy and durable parts; low shrinkage, not easy to warp and crack during printing.

Color:
Diameter Size:
Net Weight:

Introduction

Parameter Information

Notes

Download

* Description:

Description

Based on the modification of ABS material, it retains good mechanical properties, lower odor and lower shrinkage rate than conventional ABS materials.With low VOC volatile content, low odor during printing, comfortable printing without pressure; good toughness and impact resistance, it can be used to print sturdy and durable parts; low shrinkage, not easy to warp and crack during printing.

Sellingpoint

Low odor
Sturdy and durable
Heat resistance
High toughness

Low shrinkage
High impact resistance
Excellent printability

* Application
Machinery Mould Toy Automobile Electronic appliances
* Print model
  • ABS ODORLESS print model
  • ABS ODORLESS print model (2)
  • ABS ODORLESS print model
  • ABS ODORLESS print model (3)
Filament Properties Table
3D PRINTING FILAMENT ABS Odorless
Density(g/cm3) 1.04
Heat Distortion Temp(℃,0.45MPa) 73
Melt Flow Index(g/10min) 26.7(220℃/10kg)
Tensile Strength(MPa) 46.8
Elongation at Break(%) 24.4
Flexural Strength(MPa) 54.9
Flexural Modulus(MPa) 1234
IZOD Impact Strength(kJ/㎡) 24.3
Durability 8/10
Printability 8/10
Recommended printing parameters
Extruder Temperature(℃) 240 – 250℃
Recommended temperature:240℃
Bed temperature(℃)  95 – 110°C
Fan Speed  0 – 15%
Printing Speed  40 – 100mm/s
Heated Bed  Required
Recommended Build Surfaces High temperature tape, PVP solid glue
Feature
Flexible ——
Elastic ——
Impact Resistant
Soft ——
Composite ——
 UV Resistant ——
Water Resistant ——
Dissolvable ——
Heat Resistant
Chemically Resistant ——
Fatigue Resistant ——
Need drying ——
Heated Bed Required
Print recommend Minimize the overhang angle structure in the model when print in an enclosed space, and turn on the fan when it needs

1. The shrinkage rate of ABS Odorless material is large, so you should pay attention to heat preservation when printing, and print in a printer with a closed chamber.
2. The cooling of ABS Odorless is slightly worse. You can turn on a fan to improve the printing effect, or reduce the drape angle structure in the model; or try to reduce the speed to print.